Effects of fatigue on microstructure and mechanical properties of bone organic matrix under compression
PBN-AR
Instytucja
Instytut Agrofizyki im. Bohdana Dobrzańskiego Polskiej Akademii Nauk
Źródłowe zdarzenia ewaluacyjne
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Australasian Physical & Engineering Sciences in Medicine
ISSN
0158-9938
EISSN
1879-5447
Wydawca
SPRINGER
DOI
Rok publikacji
2013
Numer zeszytu
1
Strony od-do
43-54
Numer tomu
36
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
en
Acoustic emission; Anisotropy; Bovine cortical bone; Fatigue Image analysis
Open access
Tryb otwartego dostępu
Inne
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Inna
Czas opublikowania w otwartym dostępie
Data udostępnienia w sposób otwarty
Streszczenia
Język
en
Treść
The aim of the study was to investigate whether a fatigue induced weakening of cortical bone was revealed in microstructure and mechanical competence of demineralized bone matrix. Two types of cortical bone samples (plexiform and Haversian) were use. Bone slabs from the midshaft of bovine femora were subjected to cyclical bending. Fatigued and adjacent control samples were cut into cubes and demineralized in ethylenediaminetetraacetic acid. Demineralized samples were either subjected to microscopic quantitative image analysis, or compressed to failure (in longitudinal or transverse direction) with a simultaneous analysis of acoustic emission (AE). In fatigued samples porosity of organic matrix and average area of pores have risen, along with a change in the pores shape. The effect of fatigue depended on the type of the bone, being more pronounced in the plexiform than in Haversian tissue. Demineralized bone matrix was anisotropic under compressive loads in both types of cortical structure. The main result of fatigue pretreatment on mechanical parameters was a significant decrease of ultimate strain in the transverse direction in plexiform samples. The decrease of strain in this group was accompanied by a considerable increase of the fraction of large pores and a significant change in AE energy.
Cechy publikacji
ORIGINAL_ARTICLE
Inne
System-identifier
594484
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych