Magnetic order and the role of inhomogeneities in Ge1−x−yPbxCryTe bulk nanocomposite crystals
PBN-AR
Instytucja
Instytut Fizyki Polskiej Akademii Nauk
Źródłowe zdarzenia ewaluacyjne
Informacje podstawowe
Główny język publikacji
en
Czasopismo
JOURNAL OF ALLOYS AND COMPOUNDS
ISSN
0925-8388
EISSN
Wydawca
ELSEVIER SCIENCE SA
DOI
URL
Rok publikacji
2016
Numer zeszytu
Strony od-do
184–193
Numer tomu
686
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
en
Semimagnetic-semiconductors Ferromagnetic-materials Cluster-defects
Streszczenia
Język
en
Treść
We present studies of the influence of the chemical composition changes on the type of magnetic order present in bulk nanocomposite Ge1−x−yPbxCryTe crystals with the average Pb-content close to x  ≈  0.20 and Cr-content, y, varying from y  =  0.017 up to 0.043. Detailed magnetometric studies revealed the existence of two ordered magnetic states present in all our samples. All our crystals show a paramagnet to spin-glass-like state transition at temperatures from 135 K to 145 K, related to the presence of Cr5Te8 clusters in the host lattice. The second transition type depends on the Cr-content, y. In the case of samples with y equal to 0.038 and 0.043 the ferromagnetic phase is observed with TC slightly below 70 K, while in samples with lower chromium concentration the presence of spin-glass-like state slightly below 50 K is observed. The presence of clusters in our samples has significant impact on the carrier transport and magnetotransport in our samples. The presence of critical scattering on the magnetic impurities is observed in resistivity and magnetoresistance data. Nearly-linear magnetoresistance is also observed in our samples indicating a presence of strong scattering on the grain boundaries in our samples.
Cechy publikacji
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Original article
Original article presents the results of original research or experiment.
Inne
System-identifier
PBN-R:730923
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych