New synthesis route to decorate Li4Ti5O12 grains with GO flakes
PBN-AR
Instytucja
Sieć Badawcza Łukasiewicz - Instytut Elektrotechniki
Źródłowe zdarzenia ewaluacyjne
Informacje podstawowe
Główny język publikacji
en
Czasopismo
JOURNAL OF ALLOYS AND COMPOUNDS (35pkt w roku publikacji)
ISSN
0925-8388
EISSN
Wydawca
ELSEVIER SCIENCE SA
DOI
URL
Rok publikacji
2017
Numer zeszytu
Strony od-do
210-217
Numer tomu
719
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
en
Li4Ti5O12
Lithium-titanium oxide
Graphene oxide flakes
Anode
Streszczenia
Język
en
Treść
Lithium titanium oxide (Li4Ti5O12) particles were surface-decorated with 1-5\% wt. of graphene oxide (GO) using new low temperature method (LTM). All the synthesized materials have been characterized by a number of methods: X-ray powder diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atomic force microscopy (AFM). The study includes the influence of the graphene oxide flakes decoration on lithium titanium oxide crystal structure. Raman analysis demonstrates a typical spinel spectra of Li4Ti5O12 (LTO) and relatively sharp D and G lines of GO structure. The XPS measurements shows the most intense peaks at the binding energy of 284.5 eV, which corresponds to C = C/C-C in aromatic rings of GO located on the surface of Li4Ti5O12. The peaks observed at 285.8, 286.9 and 288.3 eV belong to CeO in hydroxyl and epoxy groups, carbonyl functional groups, and O-C = O in carboxyl groups, respectively. The correlation between the structural and morphological analysis of spinel Li4Ti5O12 structure decorated with graphene oxide (GO) flakes was examined for the first time in this work. (C) 2017 Elsevier B.V. All rights reserved.
Cechy publikacji
discipline:Fizyka
discipline:Physics
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:827857
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych