Effects of thermal treatments on microstructure and mechanical properties of a $Co-Cr-Mo-W$ biomedical alloy produced by laser sintering
PBN-AR
Instytucja
Wydział Inżynierii Metali i Informatyki Przemysłowej (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Źródłowe zdarzenia ewaluacyjne
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Journal of the Mechanical Behavior of Biomedical Materials
ISSN
1751-6161
EISSN
1878-0180
Wydawca
Elsevier Science BV
Rok publikacji
2016
Numer zeszytu
Strony od-do
106--117
Numer tomu
60
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.85
Autorzy
Pozostali autorzy
+ 8
Autorzy przekładu
(liczba autorów przekładu: 0)
Słowa kluczowe
EN
mechanical properties
laser sintering
Co alloys
heat treatments
structure characterisation
Streszczenia
Język
EN
Treść
Direct Metal Laser Sintering (DMLS) technology based on a layer by layer production process was used to produce a Co–Cr–Mo–W alloy specifically developed for biomedical applications. The alloy mechanical response and microstructure were investigated in the as-sintered state and after post-production thermal treatments. Roughness and hardness measurements, and tensile and flexural tests were performed to study the mechanical response of the alloy while X-ray diffraction (XRD), electron microscopy (SEM, TEM, STEM) techniques and microanalysis (EDX) were used to investigate the microstructure in different conditions. Results showed an intricate network of ε-Co (hcp) lamellae in the γ-Co (fcc) matrix responsible of the high UTS and hardness values in the as-sintered state. Thermal treatments increase volume fraction of the ε-Co (hcp) martensite but slightly modify the average size of the lamellar structure. Nevertheless, thermal treatments are capable of producing a sensible increase in UTS and hardness and a strong reduction in ductility. These latter effects were mainly attributed to the massive precipitation of an hcp Co3(Mo,W)2Si phase and the contemporary formation of Si-rich inclusions.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:095721
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych