Effect of low and high heating rates on reaction path of Ni(V)/Al multilayer
PBN-AR
Instytucja
Akademickie Centrum Materiałów i Nanotechnologii (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Źródłowe zdarzenia ewaluacyjne
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Materials Chemistry and Physics (35pkt w roku publikacji)
ISSN
0254-0584
EISSN
1879-3312
Wydawca
Elsevier Science SA
DOI
Rok publikacji
2017
Numer zeszytu
Strony od-do
244--252
Numer tomu
193
Link do pełnego tekstu
Liczba arkuszy
0.64
Słowa kluczowe
EN
microstructure
Ni(V)/Al multilayers
electron microscopy (TEM, SEM)
energy dispersive spectroscopy (EDS)
Streszczenia
Język
EN
Treść
The effect of heating rates of Ni(V)/Al NanoFoils® was investigated with transmission electron microscopy (TEM). The Ni(V)/Al were subjected to heating by using differential scanning calorimetry (DSC), in-situ TEM or electric pulse. Local chemical analysis was carried out using energy dispersive X-ray spectroscopy (EDS). Phase analysis was done with X-ray diffractions (XRD) and selected area electron diffractions (SAED). The experiments showed that slow heating in DSC results in development of separate exothermic effects at ∼230 °C, ∼280 °C and ∼390 °C, corresponding to precipitation of Al3Ni, Al3Ni2 and NiAl phases, respectively, i.e. like in vanadium free Ni/Al multilayers. Further heating to 700 °C allowed to obtain a single phase NiAl foil. The average grain size (g.s.) of NiAl phase produced in the DSC heat treated foil was comparable with the Ni(V)/Al multilayer period (∼50 nm), whereas in the case of reaction initiated with electric pulse the g.s. was in the micrometer range. Upon slow heating vanadium tends to segregate to zones parallel to the original multilayer internal interfaces, while in SHS process vanadium-rich phases precipitates at grain boundaries of the NiAl phase.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:104931
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych