Retrieval analysis of titanium nitride (TiN) coated prosthetic femoral heads articulating with polyethylene
PBN-AR
Instytucja
Sieć Badawcza Łukasiewicz - Instytut Obróbki Plastycznej
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Journal of Mechanical Behavior of Biomedical Materials
ISSN
1751-6161
EISSN
Wydawca
Elsevier B.V.
DOI
Rok publikacji
2015
Numer zeszytu
Strony od-do
127-139
Numer tomu
55
Identyfikator DOI
Liczba arkuszy
Autorzy
Pozostali autorzy
+ 2
Słowa kluczowe
angielski
titanium nitride
orthopedic implantcoating
total hiparthroplasty
coating wear
Open access
Tryb otwartego dostępu
Otwarte czasopismo
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Inna
Czas opublikowania w otwartym dostępie
Przed publikacją
Data udostępnienia w sposób otwarty
Streszczenia
Język
angielski
Treść
Data regarding in vivo performance of titanium nitride (TiN) coated prosthetic femoral heads is scarce,and available studies of older generations of implants demonstrated coating wear in vivo.That is why we conducted a retrieval analysis of 11 femor alheads (articulating in vivo for1–56 months) with TiN film formed using physical vapor deposition (PVD), to verify if coating failure is a problem in contemporary implants.Retrieved implants were examined using scanning electron microscope, coating roughness was evaluated with a contact profilometer and adhesion was tested using a Rockwell HRC test according to VDI 3824 guideline. Although no gross failure of theTiN coating was observed in our retrievals, all implants had defects typical for PVD coatings, such as pinholes, small titanium droplets and blisters with delaminated coating. In some heads the coating was contaminated with small niobium (Nb) droplets uniformly scattered on the entire surface of the film. Presence of Nb contamination was associated with an increased numberand area of other types of defects and poorer coatinga dhesion. In one component, subjected to multiple dislocations we found severe delamination and cracking of the coating, increased roughness and the presence of third bodies. Our results indicate, that although wear of the coating is lower than seen in older generations of implants, inconsistent quality of the TiN film among different implants indicates the need for strictmonitoring of themanufacturing process.
Inne
System-identifier
PX-56b46c308106eb71826e9638
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych