Effect of Backbone Variation on Properties of Fluorinated Polyimides toward Optoelectronic Applications
PBN-AR
Instytucja
Centrum Materiałów Polimerowych i Węglowych Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Macromolecular Chemistry and Physics
ISSN
1521-3935
EISSN
1521-3935
Wydawca
WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
DOI
Rok publikacji
2016
Numer zeszytu
Strony od-do
1661-1670
Numer tomu
217
Identyfikator DOI
Liczba arkuszy
Autorzy
Pozostali autorzy
+ 1
Autorzy przekładu
(liczba autorów przekładu: 0)
Słowa kluczowe
en
electrochemistry;
photoluminescence;
polyimides;
thermal properties
en
FIELD-EFFECT TRANSISTORS;
OPTICAL-PROPERTIES;
MAIN-CHAIN;
ELECTROCHROMIC CHARACTERISTICS;
AROMATIC POLYIMIDES;
EMITTING POLYMERS;
ELECTROLUMINESCENCE;
MOIETIES;
PYRIDINE;
FLUORENE
Streszczenia
Język
en
Treść
The fluorinated polyimides are synthesized from 4,4'-(hexafluoroisopropylidene) diphthalic anhydride and various diamines containing fluorene, anthraquinone, phenanthridine, stilbene, and fluorenylidene units. The polymers exhibit high glass transition temperature (T-g = 170-261 degrees C) and high thermal stability with decomposition temperatures (T-d) in the range of 320-560 degrees C and 290-520 degrees C in nitrogen atmosphere and in air, respectively. The optical properties, that is, absorption in UV-vis range and photoluminescence of obtained polyimides, are investigated in solution and in solid state as a blend with inert poly(methyl methacrylate). The polymers in solution and in solid state emit light in the range of 356-572 nm depending on the polymer structure. Additionally, the photoluminescence properties of the polyimide containing phenanthridine units in the backbone before and after protonation with HCl and methanesulfonic acid are tested in N-methyl-2-pyrrolidone solution. All polyimides are electrochemically active and undergo an electrochemical reduction process as is found in cyclic voltammetry. The lowest unoccupied molecular orbital (LUMO) levels are found in the range from -3.58 to -3.93 eV.
Cechy publikacji
oryginalny artykuł naukowy
Inne
System-identifier
PX-57b5822ac2dcd71a5c33a2fb
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych