(Bio)degradable polymers as a potential material for food packaging: studies on the (bio)degradation process of PLA/ (R,S)‑PHB rigid foils under industrial composting conditions
PBN-AR
Instytucja
Centrum Materiałów Polimerowych i Węglowych Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
European Food Research and Technology
ISSN
1438-2377
EISSN
1438-2385
Wydawca
SPRINGER
DOI
URL
Rok publikacji
2016
Numer zeszytu
6
Strony od-do
815-823
Numer tomu
242
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
en
Poly[(R,S)-3-hydroxybutyrate]; Polylactide; Packages
en
ENZYMATIC DEGRADATION; ECOTOXICOLOGICAL IMPACT; BIODEGRADABLE PLASTICS; RENEWABLE RESOURCES; POLY(LACTIC ACID); BLENDS; POLYLACTIDE; POLYESTERS; STANDARDIZATION; CRYSTALLINITY
Open access
Tryb otwartego dostępu
Otwarte czasopismo
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Creative Commons — Uznanie autorstwa
Czas opublikowania w otwartym dostępie
Razem z publikacją
Streszczenia
Język
en
Treść
The rigid foils obtained from polylactide (PLA) with synthetic poly[(R, S)-3-hydroxybutyrate] ((R, S)-PHB) can be used for production of food packages, which is important enhancement of biodegradable materials application. The biodegradable rigid packaging can be subjected to organic recycling together with food remains. The degradation of PLA and its blend with (R, S)-PHB as rigid foils were studied under industrial composting conditions. Incubation of these materials in water at 70 degrees C (hydrolytic degradation) was conducted as reference experiment. Gel permeation chromatography, electrospray mass spectrometry, nuclear magnetic resonance and differential scanning calorimetry were used to determine the progress of degradation during incubation in selected environments. The present results showed that PLA-based rigid foil degrades under industrial composting conditions. In the blends, (R, S)-PHB content was found to accelerate the degradation process under industrial composting conditions in comparison with the reference experiment. Thus, it is possible to control the degradation process by changing the composition of polymer blend.
Cechy publikacji
oryginalny artykuł naukowy
Inne
System-identifier
PX-5730823fc2dc5118019ab557
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych