Subcritical crack growth in oxide and non-oxide ceramics using the Constant Stress Rate Test
PBN-AR
Instytucja
Wydział Inżynierii Materiałowej i Ceramiki (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Processing and Application of Ceramics
ISSN
1820-6131
EISSN
Wydawca
Faculty of Technology, University of Novi Sad
DOI
URL
Rok publikacji
2015
Numer zeszytu
4
Strony od-do
187--191
Numer tomu
9
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.35
Słowa kluczowe
EN
silicon carbide
silicon nitride
alumina
zirconia
subcritical crack growth
constant stress rate
Konferencja
Indeksowana w Scopus
tak
Indeksowana w Web of Science Core Collection
tak
Liczba cytowań z Web of Science Core Collection
Nazwa konferencji (skrócona)
SM-2015
Nazwa konferencji
11th conference for young scientists in ceramics
Początek konferencji
2015-10-22
Koniec konferencji
2015-10-23
Lokalizacja konferencji
Novi Sad
Kraj konferencji
RS
Lista innych baz czasopism i abstraktów w których była indeksowana
Open access
Tryb otwartego dostępu
Otwarte czasopismo
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Creative Commons — Uznanie autorstwa-Niekomercyjne-Bez utworów zależnych
Czas opublikowania w otwartym dostępie
Razem z publikacją
Data udostępnienia w sposób otwarty
Streszczenia
Język
EN
Treść
Fracture toughness is one of the most important parameters for ceramics description. In some cases, material failure occurs at lower stresses than described by KIc parameter. On these terms, determination of fracture toughness only, proves to be insufficient. This may be due to environmental factors, such as humidity, which might cause subcritical crack propagation in a material. Therefore, it is very important to estimate crack growth velocities to predict lifetime of ceramics used under specific conditions. Constant Stress Rate Test is an indirect method of subcritical crack growth parameters estimation. Calculations are made using strength data, thus avoiding crack measurement. Expansion of flaws causes reduction of material strength. If subcritical crack growth phenomenon occurs, critical value of crack lengths increases with decreasing stress rate due to longer time for flaw to grow before the critical crack propagation at KIc takes place. Subcritical crack growth phenomenon is particularly dangerous for oxide ceramics due to chemical interactions occurring as a result of exposure to humidity. This paper presents results of Constant Stress Rate Test performed for alumina, zirconia, silicon carbide and silicon nitride in order to demonstrate the differences in subcritical crack propagation phenomenon course.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:095346
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych