Hard-template synthesis of titanium dioxide hollow spheres
PBN-AR
Instytucja
Wydział Inżynierii Materiałowej i Ceramiki (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Micro & Nano Letters
ISSN
1750-0443
EISSN
Wydawca
Institution of Engineering and Technology
Rok publikacji
2014
Numer zeszytu
10
Strony od-do
721--725
Numer tomu
9
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.4
Streszczenia
Język
EN
Treść
An easy approach for the fabrication of titanium dioxide hollow spheres is proposed. Nanostructures were obtained by the conventional hard template method with silica-protected calcination. The samples were characterised by differential thermal analysis and thermogravimetry, Brunauer-Emmett-Teller nitrogen adsorption isotherms, X-ray diffraction, scanning and transmission electron microscopy (SEM and TEM). Raman spectroscopy and optical properties of the prepared materials were studied as well. X-ray analysis has shown that the silica protection layer allows direct phase transformation from amorphous titania to crystalline anatase regardless of the temperature. The crystallite size is more than 5 nm. The diameter of the obtained hollow nanostructures is within the range 115-420 nm. The thickness of the walls varies from 12 to 38 nm depending on annealing conditions. TEM and SEM images confirm their spherical shape. © The Institution of Engineering and Technology 2014.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:085931
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych