Exchange bias effect in CaMn0.9Nb0.1O3
PBN-AR
Instytucja
Instytut Fizyki Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Materials Chemistry and Physics
ISSN
0254-0584
EISSN
Wydawca
ELSEVIER SCIENCE SA
DOI
URL
Rok publikacji
2015
Numer zeszytu
Strony od-do
170-176
Numer tomu
164
Liczba arkuszy
Słowa kluczowe
en
Magnetic materials Oxides Hysteresis Magnetic properties Magnetic structures
Streszczenia
Język
en
Treść
The exchange bias effect in CaMn0.9Nb0.1O3 has been investigated. It was found that both vertical and horizontal shifts in magnetic hysteresis loop of field cooled sample decrease monotonously with increasing temperature and vanish above 70 K, while the coercivity disappears only above 90 K, upon approaching the Neel temperature. An exponential decay successfully describes variation of the shifts with temperature. The exchange bias phenomenon is in general attributed to low-temperature phase separation into ferromagnetic clusters immersed in the G-type or C-type antiferromagnetic matrix and the resulting appearance of interfaces between coexisting different magnetic phases. Our results indicate that the exchange bias effect in CaMn0.9Nb0.1O3 may be induced, at least partially, by Dzyaloshinsky -Moriya interactions. Measurements of hysteresis loops at various cooling fields from the range -90 < H < 90 kOe show that magnetization at magnetic field H > 20 kOe exhibits a nonlinear increase and a sort of metamagnetic transition that appears to be responsible for a complete suppression of the exchange bias effect in CaMn0.9Nb0.1O3 at high magnetic field.
Cechy publikacji
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Original article
Original article presents the results of original research or experiment.
Inne
System-identifier
PBN-R:698022
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych