Effect of catalyst diameter on vapour-liquid-solid growth of GaAs nanowires
PBN-AR
Instytucja
Instytut Fizyki Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Journal of Applied Physics
ISSN
0021-8979
EISSN
1089-7550
Wydawca
AMER INST PHYSICS
DOI
URL
Rok publikacji
2014
Numer zeszytu
6
Strony od-do
063509-1-6
Numer tomu
116
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
en
MOLECULAR-BEAM EPITAXY III-V NANOWIRES LINE TENSION CONTACT-ANGLE EQUILIBRIUM MOVPE
Streszczenia
Język
en
Treść
GaAs nanowires were grown on (111)B GaAs substrates using the vapour-liquid-solid mechanism. The Au/Pt nanodots used to catalyse wire growth were defined lithographically and had varying diameter and separation. An in-depth statistical analysis of the resulting nanowires, which had a cone-like shape, was carried out. This revealed that there were two categories of nanowire present, with differing height and tapering angle. The bimodal nature of wire shape was found to depend critically on the diameter of the Au-Ga droplet atop the nanowire. Transmission electron microscopy analysis also revealed that the density of stacking faults in the wires varied considerably between the two categories of wire. It is believed that the cause of the distinction in terms of shape and crystal structure is related to the contact angle between the droplet and the solid-liquid interface. The dependency of droplet diameter on contact angle is likely related to line-tension, which is a correction to Young's equation for the contact angle of a droplet upon a surface. The fact that contact angle may influence resulting wire structure and shape has important implications for the planning of growth conditions and the preparation of wires for use in proposed devices.
Cechy publikacji
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Original article
Original article presents the results of original research or experiment.
Inne
System-identifier
PBN-R:675608
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych