Evidence for Al doping in lithium sublattice of LiFePO4
PBN-AR
Instytucja
Instytut Fizyki Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Solid State Ionics
ISSN
0167-2738
EISSN
Wydawca
ELSEVIER SCIENCE BV
DOI
URL
Rok publikacji
2015
Numer zeszytu
Strony od-do
33-38
Numer tomu
270
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
en
LiFePO4 Cathode material Li site nonstoichiometry Li-ion batteries
Streszczenia
Język
en
Treść
In this work, we applied various measurement techniques in order to evaluate the possibility of the introduction of Al and its actual level at Li site in LiFePO4 positive electrode material for Li-ion batteries. Rietveld refinement of neutron diffraction data indicated that Al is incorporated into Li site, however, in lower amount than expected, and that lithium content is substantially depressed. The observed trends were qualitatively supported by results of ICP OES analysis. In addition, the oxygen content in Li1-3xAlxFePO4 was found to decrease with Al doping. The introduction of relatively small amount of dopant could be an effective route to produce single-phase, highly lithium-deficient lithium iron phosphate. Spectroscopic methods (EXAFS and XANES) do not allow to unambiguously confirm the substitution; nevertheless, all the obtained results are compatible with the substitution taking place. Interestingly, electrochemical studies indicated improvement of the performance of a LiFePO4 cathode material upon partial substitution of lithium by aluminum, possibly as the effect of increase of concentration of lithium vacancies. (C) 2014 Elsevier By. All rights reserved.
Cechy publikacji
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Original article
Original article presents the results of original research or experiment.
Inne
System-identifier
PBN-R:714523
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych