Carbon nanotubes-polymer nanocomposites for controlled heating materials
PBN-AR
Instytucja
Wojskowy Instytut Techniki Inżynieryjnej im. profesora Józefa Kosackiego
Informacje podstawowe
Główny język publikacji
en
Czasopismo
JOURNAL OF APPLIED POLYMER SCIENCE
ISSN
0021-8995
EISSN
1097-4628
Wydawca
WILEY-BLACKWELL
DOI
URL
Rok publikacji
2016
Numer zeszytu
133
Strony od-do
44194-44200
Numer tomu
Identyfikator DOI
Liczba arkuszy
Autorzy
(liczba autorów: 2)
Słowa kluczowe
en
composites; properties and characterization; thermal properties
Streszczenia
Język
en
Treść
Nanocomposites of modified carbon nanotubes (CNT) and either polyurethane (PU), poly(vinyl acetate) (PVAc), or silicone materials were synthetized and characterized for thermal mat application. The obtained results revealed that the polymer used as a matrix had an impact on the electrical resistance of the mats. The lowest results of 32 X of resistance was registered with silicone-based mats containing 5 wt % of CNT. For the same CNT content the mats based on PVAc and PU displayed values of 55 and 60 X, respectively. The low resistance properties of silicone-based materials were due principally to the good compatibility of both polymer and functionalized CNT. Because of the low resistance values, this mat was subjected to thermovision analysis revealing that the samples reached temperature of about 60 8C in 9 min and 70 8C after 27 min of 27 Vof applied potential. The results showed an almost uniform temperature distribution in the samples’ surface with some high and low temperature spots, which were attributed to nonuniform distribution of CNT in the polymer matrix. In summary, all the obtained results confirm that silicone-CNT are very promising materials that can be used as low-voltage heating mats. VC
Cechy publikacji
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:744872
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych