Characterization of ZnAl cast alloys with Li addition
PBN-AR
Instytucja
Instytut Metalurgii i Inżynierii Materiałowej im. Aleksandra Krupkowskiego Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
MATERIALS & DESIGN
ISSN
0261-3069
EISSN
Wydawca
ELSEVIER SCI LTD
DOI
URL
Rok publikacji
2016
Numer zeszytu
Strony od-do
51-59
Numer tomu
104
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0,56
Autorzy
(liczba autorów: 2)
Pozostali autorzy
+ 1
Słowa kluczowe
en
Zn–Al–Li alloys; Soldering materials; Scanning electron microscopy; Transmission electron microscopy; Microstructure; Thermal expansion; Electrical resistivity; Mechanical properties
Streszczenia
Język
en
Treść
The addition of Li to eutectic ZnAl alloy caused improved mechanical and thermal properties, with potential application in new design materials used in the automotive and aerospace industries. The alloys with 0.05, 0.1, 0.2, 0.5 and 1.0 Li (wt.%) content were studied using calorimetry, to determine the melting temperatures. Thermal linear expansion and electrical resistivity measurements were performed at temperatures of − 50 °C to 300 °C and 30 °C to 300 °C. The microstructure of the specimens was analyzed using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Chemical microanalysis was performed using energy-dispersive X-ray spectroscopy (EDS) on SEM and TEM. The possibility of the occurrence of Al–Li, Li–Zn and Al–Li–Zn precipitates was studied by X-ray diffraction (XRDs) and selected area electron diffraction (SAED). The addition of Li to eutectic ZnAl alloy increased the electrical resistivity and the coefficient of thermal expansion; however, the melting point did not change. The mechanical properties, strain and microhardness increased with Li content in alloys.
Cechy publikacji
ORIGINAL_ARTICLE
Inne
System-identifier
739682
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych