Comparative XPS analyses of passive layers composition formed on duplex 2205 SS after standard and high-current-density electropolishing
PBN-AR
Instytucja
Wydział Mechaniczny (Politechnika Koszalińska)
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Tehnicki Vjesnik-Technical Gazette
ISSN
1330-3651
EISSN
Wydawca
UNIV OSIJEK, TECH FAC
DOI
URL
Rok publikacji
2016
Numer zeszytu
3
Strony od-do
731-735
Numer tomu
23
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
Autorzy
(liczba autorów: 4)
Pozostali autorzy
+ 2
Słowa kluczowe
en
Duplex 2205 SS; electropolishing; XPS Analysis
Streszczenia
Język
en
Treść
In the paper, there are described XPS results of passive layers formed on duplex 2205 (EN 1.4462) stainless steel after a standard (EP50) and high-current density electropolishing (EP1000). The electrolyte based on orthophosphoric and sulfuric acids in proportion 1:4 was used. The survey and high resolution spectra of Cr 2p, Fe 2p, S 2p, P 2p are presented in the paper. Based on the survey of XPS spectrum it was possible to find the contamination of outer sublayer consists mainly of nitrogen, sodium, chloride, potassium and partly oxygen and the inner passive sub-layer consists of iron, chromium, nickel, molybdenum, manganese, phosphorus, sulfur, silicon and partly oxygen. The obtained results show that in the passive layers formed on duplex 2205 stainless steel after a standard (EP50) and high-current density electropolishing (EP1000), the following oxides (FeO, Fe2O3, Fe3O4, Cr2O3), hydroxides (FeOOH, Cr(OH)3, CrOOH) and salts (FeSO4, Fe2(SO4)3, FePO4, CrPO4, Cr2(SO4)3) were detected. In the paper, besides iron and chromium compounds identification the authors propose two coefficients for passive surface characterization, i.e. chromium-to-iron coefficient (Cr/Fe) and phosphorus-to-sulfur (P/S). These two ratios obtained after the standard electropolishing (EP50) of 2205 SS are higher than those obtained after EP1000 treatment.
Cechy publikacji
discipline:Budowa i eksploatacja maszyn
discipline:Inżynieria materiałowa
discipline:Machinery construction and operation
discipline:Materials science
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:790482
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych