ENHANCED BIOACTIVITY OF CALCIUM PHOSPHATE COATINGS OBTAINED BY A DIRECT ELECTRODEPOSITION FROM HANKS' SOLUTION ON Ti SURFACE
PBN-AR
Instytucja
Instytut Chemii Fizycznej Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
ARCHIVES OF METALLURGY AND MATERIALS
ISSN
1733-3490
EISSN
Wydawca
POLISH ACAD SCIENCES COMMITTEE METALLURGY and INSTITUTE OF METALLURGY AND MATERIALS SCIENCE
DOI
Rok publikacji
2013
Numer zeszytu
1
Strony od-do
261-267
Numer tomu
58
Identyfikator DOI
Liczba arkuszy
Autorzy
Pozostali autorzy
+ 2
Słowa kluczowe
en
biocompatibility
Ca-P coatings
electrodeposition
BSA protein
osteoblasts (U2OS)
Open access
Tryb otwartego dostępu
Otwarte czasopismo
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Inna
Czas opublikowania w otwartym dostępie
Razem z publikacją
Data udostępnienia w sposób otwarty
Streszczenia
Język
en
Treść
The main requirements for titanium biomaterials are: (a) biocompatibility, (b) resistance to biological corrosion and (c) antisepticity. These requirements may be met by a new generation of titanium biomaterials with a specific surface layer of strictly defined microstructure, chemical and phase composition. Recently, various surface modifications have been applied to form a bioactive layer on Ti surface, which is known to accelerate osseointegration. The purpose of this study was to investigate bioactivity of porous calcium phosphate coatings prepared by a direct electrodeposition on Ti surface from a modified Hanks' solution. The thick 200 nm coatings, were prepared via cathodic polarization at constant voltage -1.5 V vs. OCP in a Hanks' solution. In order to evaluate the potential use of the coatings for biomedical applications, the adsorption of bovine serum albumin (BSA), the most abundant protein in blood, and living cells attachment (osteoblasts, U2OS) were studied. The observed differences in living cells attachment suggest a more promising initial cellular response of Ca-P coatings with a pre-adsorbed albumin. The topography and a cross-section view of the Ca-P coatings were characterized using SEM and STEM techniques. The surface analytical techniques (AES, XPS, and FTIR) were used to characterize their chemical composition before and after protein BSA adsorption.
Cechy publikacji
ORIGINAL_ARTICLE
Inne
System-identifier
763850
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych