Plasma carburizing for improvement of Ni-Fe cathodes for alkaline water electrolysis
PBN-AR
Instytucja
Wydział Matematyczno-Przyrodniczy.Szkoła Nauk Ścisłych (Uniwersytet Kardynała Stefana Wyszyńskiego w Warszawie)
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Electrochimica Acta
ISSN
0013-4686
EISSN
Wydawca
PERGAMON-ELSEVIER SCIENCE LTD
DOI
URL
Rok publikacji
2016
Numer zeszytu
Strony od-do
11 - 19
Numer tomu
220
Liczba arkuszy
Słowa kluczowe
en
water electrolysis
Ni-Fe cathodes
plasma carburizing
Streszczenia
Język
en
Treść
Abstract Electrodeposited Ni-Fe-C alloys have high electroactivity for hydrogen evolution reaction (HER) in alkaline water electrolysis. In the present work carbon was introduced into Ni and Ni–Fe alloys by plasma treatment in CH4 + H2 gas mixture at 470 °C. Despite of a very low solubility of carbon in nickel, carbon entered into nickel to the depth of about 0.5 μm. In high-Fe alloys it formed a carbide layer about 2-μm thick and increased surface hardness. Electrochemical measurements in 25 wt.% KOH at 80 °C showed that carburization resulted in an improvement of catalytic activity toward HER, especially of Ni and 1Ni-Fe. Carburization also increased the resistance to corrosion during cathodic polarisation and under open-circuit conditions. XPS surface analysis showed that after corrosion the oxide content on carburized materials was significantly lower than that on untreated materials. It is suggested that the enhanced electroactivity of plasma carburized cathodes was due mainly to the enlargement of the surface area of disintegrated material. Also, a catalytic effect might be exerted by carbon-metal particles.
Cechy publikacji
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:766399
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych