Electrophoretic deposition and characterization of HA/chitosan nanocomposite coatings on Ti6Al7Nb alloy
PBN-AR
Instytucja
Instytut Wysokich Ciśnień Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Metals and Materials International
ISSN
1598-9623
EISSN
2005-4149
Wydawca
The Korean Institute of Metals and Materials
Rok publikacji
2015
Numer zeszytu
1
Strony od-do
96-103
Numer tomu
21
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
en
biomaterials
coating
surface modification
microstructure
transmission electron microscopy (TEM)
Streszczenia
Język
en
Treść
Nano-hydroxyapatite/chitosan (nc-HA/chitosan) composite coatings were produced on two phase (α+β) Ti6Al7Nb titanium alloy substrates by electrophoretic deposition (EPD). The microstructure of the coatings was examined by scanning- and transmission electron microscopy methods as well as by X-ray diffractometry. The coatings, 770 nm–800 nm thick, were uniform, without any cracks or presence of large voids and they exhibited good adhesion to the titanium alloy substrate. The microstructure of the coatings consisted of nc-HA needle-like particles homogeneously embedded in a chitosan matrix. The deposited coatings exhibited good adhesion to the substrate. The best adhesion to the titanium alloy was determined for the coating deposited from suspensions containing 4 g/L of HA at 10 V during 240 s. The results confirm EPD as a convenient method to develop uniform and crack-free nanoscale organic-inorganic composite coatings on two phase titanium alloy substrates with potential application in orthopedic and dental implants.
Cechy publikacji
discipline:Inżynieria materiałowa
discipline:Materials science
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:751013
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych