High temperature gaseous corrosion resiatance of MgO-containing refractories - A comparative study
PBN-AR
Instytucja
Sieć Badawcza Łukasiewicz - Instytut Ceramiki i Materiałów Budowlanych
Informacje podstawowe
Główny język publikacji
en
Czasopismo
CERAMICS INTERNATIONAL
ISSN
0272-8842
EISSN
Wydawca
ELSEVIER SCI LTD
DOI
URL
Rok publikacji
2016
Numer zeszytu
14
Strony od-do
15805-15810
Numer tomu
42
Identyfikator DOI
Liczba arkuszy
Autorzy
(liczba autorów: 4)
Pozostali autorzy
+ 1
Autorzy przekładu
(liczba autorów przekładu: 0)
Słowa kluczowe
en
C. Corrosion
C. Life time
D. MgO
E. Refractories
Open access
Tryb otwartego dostępu
Otwarte czasopismo
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Inna
Czas opublikowania w otwartym dostępie
Przed publikacją
Streszczenia
Język
en
Treść
In the work the results of investigations into corrosive resistance to the attack of sulphur oxides of six commercially available basic refractories containing magnesium oxide have been presented. The research was conducted for materials applied in glass furnace regenerators: three types of magnesia-zirconia-forsterite products, one magnesia-forsterite and one magnesia product as well as a magnesia-chromite product to be applied in copper convertors. Investigations were carried out in a semi-flow chemical reactor. Investigations into corrosive resistance were conducted at 600 °C, 800 °C and 1000 °C. The real and equilibrium composition of gaseous phase in the reactor versus temperature was determined. It was assumed that the relative increment of the tested products' mass after a certain time of their staying in the reactor would be and indicator of corrosive resistance. Based on investigations into the phase composition of the products of reaction, it was found that at 600 °C and 800 °C the product's corrosion resulted from the formation of MgSO4, as the main product of reaction, whereas at 1000 °C – it was the formation of CaMg2(SO4)3. In products with an addition of ZrO2 destabilisation of the regular structure of c-ZrO2 was observed as well as its change into the monoclinic variety - m-ZrO2. The examined refractory materials were ordered according to their corrosive resistance to sulphur oxides at particular temperatures applied in the test. The conducted investigations qualitatively describe the behaviour of refractories exposed to the corrosive attack of sulphur oxides and can be useful in the selection of refractory materials for particular industrial applications.
Cechy publikacji
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:755560
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych