Effect of heating rate on phase transformations during tempering of $Mn-Cr-Mo$ alloy steels
PBN-AR
Instytucja
Wydział Inżynierii Metali i Informatyki Przemysłowej (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Książka
Tytuł książki
Metal 2013. 22\textsuperscript{nd} international conference on Metallurgy and materials : May 15\textsuperscript{th}–17\textsuperscript{th} 2013, Brno : conference proceedings
Data publikacji
2013
ISBN
978-80-87294-41-3
Wydawca
TANGER Ltd.
Publikacja
Główny język publikacji
EN
Tytuł rozdziału
Effect of heating rate on phase transformations during tempering of $Mn-Cr-Mo$ alloy steels
Rok publikacji
2013
Strony (od-do)
700--705
Numer rozdziału
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.35
Hasło encyklopedyczne
Autorzy
(liczba autorów: 3)
Pozostali autorzy
+ 1
Konferencja
Indeksowana w Scopus
tak
Indeksowana w Web of Science Core Collection
tak
Liczba cytowań z Web of Science Core Collection
Nazwa konferencji (skrócona)
Metal 2013
Nazwa konferencji
22nd International Conference on Metallurgy and Materials
Początek konferencji
2013-05-15
Koniec konferencji
2013-05-17
Lokalizacja konferencji
Brno
Kraj konferencji
CZ
Lista innych baz czasopism i abstraktów w których była indeksowana
Streszczenia
Język
EN
Treść
The hereby work presents the influence of heating rate on the phase transformations during tempering. The tempering of the as-quenched samples of two Cr-Mn-Mo model alloys with different carbon content was made at 350 degrees C. The temperature 350 degrees C was chosen because the irreversible temper brittleness effect occurs. The investigations of phase transformations during tempering of the steels were made on the grounds of dilatometric curves recorded during heating from as-quenched state. Heating to 350 degrees C was made with two different heating rates (150 degrees C/s and 5 degrees C/s). Dilatometric investigations were performed by use of the DT 1000 dilatometer made by Adamel, and L78 R. I. T. A. (Rapid Intensive Thermal Analysis) dilatometer made by Linseis. The methodology of the dilatometric investigation and the method of the characteristic points determination were described. As it is known, the temperatures of starting and ending of individual phase transformations increase with the heating rate increase. It is possible to obtain a difference in the advancement of various phase transformations during tempering, through different heating rates to the selected temperatures. It is possible to reduce probability of the occurrence of some phase transformations (e. g. transition carbides) in favor of other (e. g. cementite carbides). The difference in advancement of the various phase transformations can effects on various mechanical properties of the steels above all toughness and hardness.