Mechanical properties of hybrid Cr, Mn, and Si-containing PM steel when sintered in a local micro-atmosphere
PBN-AR
Instytucja
Wydział Inżynierii Metali i Informatyki Przemysłowej (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Kovove Materialy = Metallic Materials
ISSN
0023-432X
EISSN
1338-4252
Wydawca
Redakcia Kovove Materialy
Rok publikacji
2016
Numer zeszytu
4
Strony od-do
269--278
Numer tomu
54
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.71
Autorzy
(liczba autorów: 1)
Słowa kluczowe
EN
sintered steels
alloying elements
sintering atmospheres
Streszczenia
Język
EN
Treść
Fe-1.4Cr-1.3Ni-0.7Mn-0.2Mo-0.2Si-(0.5-0.6)C steel was sintered in semi-closed containers at 1120 or 1250 °C using nitrogen or air as the furnace gas and also conventionally sintered in N2-5%H2. Additives, principally ferromanganese, the source of Mn vapour, aluminium or naphthalene, the source of nascent carbon, and activators were included with the specimens. Sintered density, carbon, oxygen and nitrogen contents were evaluated before mechanical testing. All mechanical properties obtained with semi-closed container sintering outperformed those resulting from comparable conventional sintering. The best combination of properties resulted from liquid phase sintering at 1250 °C in N2 with naphthalene/Na2CO3 or Al/NH4I/NaCl/AlCl3 additives. Properties included strain-to-failure of ∼ 4.5 %, the yield stress of 374 and tensile strength of 813 MPa. Results for air as the furnace gas were slightly inferior. This opens up the possibility of using conventional air furnaces for sintering ceramics to process PM steels to (near) full density to match the properties of their wrought counterparts.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:099308
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych