Translucent zirconia polycrystals prepared from nanometric powders
PBN-AR
Instytucja
Wydział Inżynierii Materiałowej i Ceramiki (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Processing and Application of Ceramics
ISSN
1820-6131
EISSN
Wydawca
Faculty of Technology, University of Novi Sad
DOI
URL
Rok publikacji
2015
Numer zeszytu
3
Strony od-do
175--180
Numer tomu
9
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.42
Słowa kluczowe
EN
translucence ceramics
yttria stabilised zirconia
nanometric powders
Open access
Tryb otwartego dostępu
Otwarte czasopismo
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Creative Commons — Uznanie autorstwa-Niekomercyjne-Bez utworów zależnych
Czas opublikowania w otwartym dostępie
Razem z publikacją
Data udostępnienia w sposób otwarty
Streszczenia
Język
EN
Treść
The aim of the present study was investigation of synthesis and sinterability of nanometric zirconia solid solution powders containing 8 mol% and 3 mol% of Y2O3 . The powders were prepared by the hydrothermal treatment of the co-precipitated gels, which resulted in very fine powders with particle sizes <10 nm. The main problem in application of such fine powders is their tendency to form hard agglomerates. To overcome this obstacle, the aqueous suspensions of the powders were subjected to the freeze drying. It resulted in the powders composed of very weak agglomerates which were broken under pressure as low as ∼1 MPa. The powder compacts were sintered in oxygen atmosphere to the state of closed porosity and then HIP-ed at 1300 °C to fully dense ceramics. The spectrophotometric investigations in the wave length range of 190–1100 nm indicated higher translucency of the 8 mol% Y2O3-ZrO2 than the 3 mol% Y2O3-ZrO2 ceramics. Most probably it should be related to the birefringence phenomenon which occurs in the latter case due to the tetragonal symmetry of this material. In the polycrystal containing 8 mol% of Y2O3 this phenomenon does not occur due to its cubic symmetry. The other two factors which lead to the decreased optical transparency of the material containing 3 mol% Y2O3 are its smaller grain sizes and the presence of some amount of the monoclinic phase.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:100532
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych