Description of subcritical crack growth phenomenon in alumina-zirconia particulate composites using parameters determined by the constant stress rate test
PBN-AR
Instytucja
Wydział Inżynierii Materiałowej i Ceramiki (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Książka
Tytuł książki
Brittle Matrix Composites 11. [proceedings of the 11\textsuperscript{th} international symposium on Brittle Matrix Composites (BMC-11) : Warsaw, September 28–30, 2015]
Data publikacji
2015
ISBN
978-83-89687-96-8
Wydawca
IFTR
Publikacja
Główny język publikacji
EN
Tytuł rozdziału
Description of subcritical crack growth phenomenon in alumina-zirconia particulate composites using parameters determined by the constant stress rate test
Rok publikacji
2015
Strony (od-do)
83--90
Numer rozdziału
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.57
Hasło encyklopedyczne
Słowa kluczowe
EN
Zirconia toughened alumina
subcritical crack growth
strength tests
Konferencja
Indeksowana w Scopus
tak
Indeksowana w Web of Science Core Collection
tak
Liczba cytowań z Web of Science Core Collection
Nazwa konferencji (skrócona)
BMC 11
Nazwa konferencji
Brittle Matrix Composites 11
Początek konferencji
2015-09-28
Koniec konferencji
2015-09-30
Lokalizacja konferencji
Warszawa
Kraj konferencji
PL
Lista innych baz czasopism i abstraktów w których była indeksowana
Streszczenia
Język
EN
Treść
Ceramic elements should serve under loads, which are causing stresses lower than the critical ones. Even though these stresses are lower, flaws dimensions might be not stable. That is why, crack velocity determination is important for estimation of ceramics lifetime. Environmental factors, such as humidity or temperature, have a major impact on a material strength. It happens due to occurrence of the subcritical crack growth. It is commonly observed that failure stress of a material might be lower than the one predicted from the K-Ic factor determined in standard dynamic tests. Constant Stress Rate Test uses strength measurements at different stress rates to deduce subcritical crack growth parameters. Lower stress rate gives more time for flaws to grow. It follows that failure stress increases with increasing stress rate. Investigation was made for three composites: 5 vol. % of tetragonal zirconia isolated in the alumina matrix, alumina with 15 vol. % of tetragonal zirconia, which was a content near the percolation point and a typical duplex microstructure with a 50 vol. % of each phase. Alumina sinters were used as a reference material.