Ammonical leaching and recovery of copper from alloyed low-grade e-waste
PBN-AR
Instytucja
Wydział Metali Nieżelaznych (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Journal of Material Cycles and Waste Management
ISSN
1438-4957
EISSN
Wydawca
Springer
DOI
Rok publikacji
2016
Numer zeszytu
2
Strony od-do
318--328
Numer tomu
18
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.78
Autorzy
Słowa kluczowe
EN
copper
recovery
electrolysis
ammoniacal leaching
e-waste
Open access
Tryb otwartego dostępu
Otwarte czasopismo
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Creative Commons — Uznanie autorstwa
Czas opublikowania w otwartym dostępie
Razem z publikacją
Data udostępnienia w sposób otwarty
Streszczenia
Język
EN
Treść
The paper concerns a hydrometallurgical method for selective recovery of copper from low-grade electric and electronic wastes. The following consecutive stages were proposed: smelting of the scraps to produce Cu-Zn-Ag alloy, leaching of the alloy in ammoniacal solution, and selective copper electrowinning. Cu-Zn-Ag alloy was a polymetallic and five-phase system. It was leached in chloride, carbonate, sulfate and thiosulfate solutions. This resulted in the separation of the metals, wherein metallic tin and silver as well as lead salts remained in the slimes, while copper and zinc were transferred to the electrolyte. Copper was selectively recovered from the ammoniacal solutions by the electrolysis, leaving zinc ions in the electrolyte. The best conditions of the alloy treatment were obtained in the ammonia-carbonate system, where the final product was copper of high purity (99.9 %) at the current efficiency of 60 %. Thiosulfate solution was not applicable for the leaching of the copper alloy due to secondary reactions of the formation of copper(I) thiosulfate complexes and precipitation of copper(I) sulfide, both inhibiting dissolution of the metallic material.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:101272
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych