Bulk nanomaterials and powders consolidation produced by Cyclic Extrusion Compression
PBN-AR
Instytucja
Wydział Metali Nieżelaznych (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Key Engineering Materials
ISSN
1013-9826
EISSN
1662-9795
Wydawca
Trans Tech Publications
DOI
Rok publikacji
2016
Numer zeszytu
Strony od-do
276--283
Numer tomu
682
Link do pełnego tekstu
Liczba arkuszy
0.5
Słowa kluczowe
EN
nanostructures
powder consolidation
cyclic extrusion compression
severe plastic deformation methods
Konferencja
Indeksowana w Scopus
tak
Indeksowana w Web of Science Core Collection
nie
Liczba cytowań z Web of Science Core Collection
Nazwa konferencji (skrócona)
ICNFM'15
Nazwa konferencji
Engineering and Technology on Non-Ferrous Metals : 2nd international conference
Początek konferencji
2015-06-22
Koniec konferencji
2015-06-24
Lokalizacja konferencji
Cracow
Kraj konferencji
PL
Lista innych baz czasopism i abstraktów w których była indeksowana
Streszczenia
Język
EN
Treść
The cyclic extrusion compression - reciprocating extrusion process is one of severe plastic deformation methods, which allow to produce bulk nanomaterials without changing the initial shape of deformed samples. The results are presented showing that the average grains size and microbands thickness in aluminium alloys decrease below 100 nm. The investigations revealed that the average grains size is about 250 nm and 200 nm in polycrystalline and monocrystalline copper, respectively. The cyclic extrusion compression method is also used to produce bulk materials by powder consolidation. The subgrains/nanograins inside the silver powder particles after the consolidation processes achieved the mean size of about 100 nm. Moreover, it has been found that inside structure observed by TEM, the consolidated powder granules consisted from nanometric twins of about 10-20 nm. This silver based powder consolidated by cyclic extrusion compression method were extruded by hydrostatic extrusion method. The final product were the wires with a diameter of 3 mm, which were used to electrical contacts production. © 2016 Trans Tech Publications.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:096215
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych