Characterisation of oxide coatings produced on aluminium by PEO at different frequencies of pulsed current
PBN-AR
Instytucja
Wydział Metali Nieżelaznych (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Materials Science Forum
ISSN
0255-5476
EISSN
1662-9752
Wydawca
Trans Tech Publications
DOI
Rok publikacji
2015
Numer zeszytu
Strony od-do
427--432
Numer tomu
828-829
Link do pełnego tekstu
Liczba arkuszy
0.42
Słowa kluczowe
EN
microstructure
coatings
plasma electrolytic oxidation
aluminium oxide
X-ray diffraction
Konferencja
Indeksowana w Scopus
tak
Indeksowana w Web of Science Core Collection
nie
Liczba cytowań z Web of Science Core Collection
Nazwa konferencji (skrócona)
LMT 2015
Nazwa konferencji
7th International Light Metals Technology Conference
Początek konferencji
2015-07-27
Koniec konferencji
2015-07-29
Lokalizacja konferencji
Port Elisabeth
Kraj konferencji
ZA
Lista innych baz czasopism i abstraktów w których była indeksowana
Streszczenia
Język
EN
Treść
The Plasma Electrolytic Oxidation (PEO) is a surface modification process that allows producing protective oxide coatings on light metal alloys. These coatings are characterized by high microhardness and wear resistance. Changes of electrical conditions of alternate current during process, such as duration and frequency of anodic and cathodic pulses, influence on layer growth rate, its microstructure and final properties. In this study aluminium samples were oxidized at different electrical parameters in sodium silicate electrolyte. The growth rates of oxide layers were determined by mass change and thickness measurements. The microstructure of the obtained coatings was investigated by using scanning electron microscope. Additionally, phase compositions of coatings was determined by X-ray diffraction on top surfaces of layers. Generally, shorter duration and higher frequency of anodic pulses provides more uniform structure at lower growth rate. Nevertheless, there are certain ranges of electrical parameters that provide decent uniformity of oxide coatings. © (2015) Trans Tech Publications, Switzerland.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:091510
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych