Recycling without melting: an alternative approach to aluminum scrap recovery
PBN-AR
Instytucja
Wydział Metali Nieżelaznych (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Key Engineering Materials
ISSN
1013-9826
EISSN
1662-9795
Wydawca
Trans Tech Publications
DOI
Rok publikacji
2016
Numer zeszytu
Strony od-do
284--289
Numer tomu
682
Link do pełnego tekstu
Liczba arkuszy
0.4
Autorzy
Pozostali autorzy
+ 1
Słowa kluczowe
EN
recycling
aluminium alloy
plastic consolidation
coolant removal
Konferencja
Indeksowana w Scopus
tak
Indeksowana w Web of Science Core Collection
nie
Liczba cytowań z Web of Science Core Collection
Nazwa konferencji (skrócona)
ICNFM'15
Nazwa konferencji
Engineering and Technology on Non-Ferrous Metals : 2nd international conference
Początek konferencji
2015-06-22
Koniec konferencji
2015-06-24
Lokalizacja konferencji
Cracow
Kraj konferencji
PL
Lista innych baz czasopism i abstraktów w których była indeksowana
Streszczenia
Język
EN
Treść
Method of scrap recovery by hot extrusion in a contrast to traditional aluminum recycling process distinguishes itself with a low energy consumption and high recovery efficiency. Additionally, this type of recycling allows to recover materials even from highly fragmented forms of metal like chips, foils or filings by omitting melting procedure. In the present study results of 413.0 aluminum chips plastic consolidation will be presented. Chips after machining process were used as a charge material for the entire recycling process. In order to determined the best emulsion elimination method, three separate processes such as centrifugation, annealing and pressing were carried out. In result dry, wet and cleaned chips in a form of cylindrical billets were hot extruded into longitudinal square cross-section profiles. Mechanical properties were examined by uniaxial tensile tests while microstructure observations were performed by means of scanning electron microscopy. It has been showed that emulsion elimination by annealing gives the best results while at the same time all extruded materials revealed no significant differences in mechanical properties. © 2016 Trans Tech Publications.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:096219
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych