The influence of extrusion ratio on the strenght of hot extruded aluminium alloy chips
PBN-AR
Instytucja
Wydział Metali Nieżelaznych (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Książka
Tytuł książki
Metal 2015 : 24\textsuperscript{th} international conference on Metallurgy and materials : June 3\textsuperscript{rd}–5\textsuperscript{th} 2015, Brno, Czech Republic : proceedings
Data publikacji
2015
ISBN
978-80-87294-58-1
Wydawca
TANGER Ltd.
Publikacja
Główny język publikacji
EN
Tytuł rozdziału
The influence of extrusion ratio on the strenght of hot extruded aluminium alloy chips
Rok publikacji
2015
Strony (od-do)
1600--1604
Numer rozdziału
Link do pełnego tekstu
Identyfikator DOI
Liczba arkuszy
0.42
Hasło encyklopedyczne
Autorzy
Słowa kluczowe
EN
plastic consolidation
aluminum chips
recycling aluminum alloys
Konferencja
Indeksowana w Scopus
nie
Indeksowana w Web of Science Core Collection
tak
Liczba cytowań z Web of Science Core Collection
Nazwa konferencji (skrócona)
Metal 2015
Nazwa konferencji
24th international conference on Metallurgy and materials
Początek konferencji
2015-06-03
Koniec konferencji
2015-06-05
Lokalizacja konferencji
Brno
Kraj konferencji
CZ
Lista innych baz czasopism i abstraktów w których była indeksowana
Streszczenia
Język
EN
Treść
Hot-extrusion of the chips and other highly fragmented materials is a very convenient way for aluminum alloys scarp processing. It is possible to achieve ready or semi-finished products in one step of material forming directly from the chips to the bulk material. The mechanical properties of such processed material are affected by various extrusion conditions: temperature, extrusion speed and cross-section reduction ratio.. The variation of cross-section reduction ratio has an effect on chips bonding quality, which in turn results in different mechanical properties. The objective of the present study is to analyze mechanical and structural features of 6060 and AlSi11 aluminum alloys after plastic consolidation by hot extrusion with different cross-section reduction ratio in the range of 7 to 45. Aluminum alloy in the form of chips, were preliminarily cold compacted to produce cylindrical billets. The as-compressed billets were then hot extruded at 450 degrees C. The samples cut from as extruded rods were subjected to tensile test and structural SEM observations. Based on obtained results minimum extrusion ratio required for sound bonding of chips was established.