Characterization of structural, thermal and mechanical properties of bismuth silicate glasses
PBN-AR
Instytucja
Wydział Fizyki Technicznej i Matematyki Stosowanej (Politechnika Gdańska)
Informacje podstawowe
Główny język publikacji
ENG
Czasopismo
JOURNAL OF NON-CRYSTALLINE SOLIDS
ISSN
0022-3093
EISSN
Wydawca
DOI
URL
Rok publikacji
2016
Numer zeszytu
Strony od-do
51-56
Numer tomu
439
Liczba arkuszy
Słowa kluczowe
BISMUTH-SILICATE GLASS
DIFFERENTIAL SCANNING CALORIMETRY
NANOINDENTATION
REDUCTION
Streszczenia
Język
Treść
he influence of heating and reduction processes on the structural, thermal and mechanical properties of bismuth-silicate glasses has been investigated. Two compositions of glasses: 40Bi2O3–60SiO2 (Bi0.57Si0.43Ox) and 27Bi2O3–73SiO2 (Bi0.43Si0.57Ox) were fabricated by a typical melt quenching technique. Then the reduction in hydrogen at 380 °C for 20, 42 or 67 h was performed. It was found that a 50 μm-thick layer was formed on the glass surface after reduction process. It was confirmed that this layer is formed by granules of metallic bismuth embedded in a glass matrix. The DSC measurements confirmed that melting of metallic bismuth takes place during heating of a previously reduced glass sample. It was also found that heat treatment process influences hardness and Young modulus of Bi–Si–O glass.
Inne
System-identifier
136647
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych