Structure and thermoelectric properties of Bi–Te alloys obtained by novel method of oxide substrates reduction
PBN-AR
Instytucja
Wydział Fizyki Technicznej i Matematyki Stosowanej (Politechnika Gdańska)
Informacje podstawowe
Główny język publikacji
ENG
Czasopismo
JOURNAL OF ALLOYS AND COMPOUNDS
ISSN
0925-8388
EISSN
Wydawca
DOI
URL
Rok publikacji
2015
Numer zeszytu
15
Strony od-do
1124-1132
Numer tomu
646
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
BISMUTH–TELLURIUM ALLOY
FIGURE OF MERIT
OXIDES REDUCTION
THERMOELECTRIC
Streszczenia
Język
Treść
A novel method of thermoelectric materials fabrication has been developed. Oxide reagents have been melted at high temperature in air, quenched, milled to powder and reduced in hydrogen to form Bi–Te alloys. Structural and thermoelectric properties of samples have been investigated depending on initial composition and temperature of reduction process. Sample 25Bi2O3–75TeO2 reduced at 340 °C for 10 h has been found to be a p-type conductor, whereas the other are n-type conductors. The highest figure of merit (ZT = 0.2) at near-room temperature shows the 20Bi2O3–80TeO2 compound reduced at 400 °C for 10 h. The suggested novel method of thermoelectric materials fabrication is cheap, easy and allows to control the composition and microstructure (size of grains, distribution etc.) in order to obtain both high electrical conductivity and relatively low thermal conductivity of final product.
Inne
System-identifier
133686
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych