Luminescent properties of ZnO and ZnMgO epitaxial layers under high hydrostatic pressure
PBN-AR
Instytucja
Wydział Fizyki (Politechnika Warszawska)
Informacje podstawowe
Główny język publikacji
en
Czasopismo
JOURNAL OF ALLOYS AND COMPOUNDS
ISSN
0925-8388
EISSN
Wydawca
ELSEVIER SCIENCE SA
DOI
URL
Rok publikacji
2016
Numer zeszytu
Strony od-do
125-130
Numer tomu
672
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
en
Oxide materials
Semiconductors
Optical properties
Phase transitions
High-pressure
Optical spectroscopy
Luminescence
Streszczenia
Język
en
Treść
Studies of ambient-pressure and high-pressure behaviour of photoluminescence (PL) as well as the phase transition pressure from wurtzite to cubic structure for a series of Zn1−xMgxO alloys as a function of the Mg-content x (0 ≤ x ≤ 0.34) are presented. The measured PL peak energy is shown to increase approximately linearly with increasing magnesium content from 3.36 eV to 4.11 eV, and the phase transition pressure from wurtzite to cubic structure decreases with increasing x from 12.6 GPa to 5.9 GPa. The phase transition is accompanied by a strong decrease of the near band-gap PL intensity. The value of the PL peak pressure coefficient dEPL/dp changes non-monotonically. It varies between 18.6 meV/GPa and 25.2 meV/GPa, and seems to depend on the layer thickness rather than on the layer composition, exhibiting strong scattering for several alloys with similar magnesium content. This behaviour can be due to the stabilizing influence of sapphire substrate, as is indicated both by the pressure coefficients and by the values of pressure of phase transition from wurtzite to rock salt structure in Zn1−xMgxO layers with the same or similar composition and different layer thicknesses.
Cechy publikacji
discipline:Fizyka
discipline:Physics
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:729065
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych