Enhanced mid-infrared 2.7 μm luminescence in low hydroxide bismuth-germanate glass and optical fiber co-doped with ${Er^{3 +}}$ /${Yb^{3 +}}$ ions
PBN-AR
Instytucja
Wydział Inżynierii Materiałowej i Ceramiki (Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie)
Informacje podstawowe
Główny język publikacji
EN
Czasopismo
Journal of Non-Crystalline Solids (30pkt w roku publikacji)
ISSN
0022-3093
EISSN
1873-4812
Wydawca
Elsevier Science BV
DOI
Rok publikacji
2017
Numer zeszytu
Strony od-do
169--174
Numer tomu
457
Link do pełnego tekstu
Liczba arkuszy
0.4
Autorzy
Pozostali autorzy
+ 4
Autorzy przekładu
(liczba autorów przekładu: 0)
Słowa kluczowe
EN
rare earth elements
2.7 μm emission
mid-infrared
heavy metal oxide
bismuth-germanate
Er 3+ /Yb 3+
optical active fiber
Streszczenia
Język
EN
Treść
In this article, low hydroxide bismuth-germanate glasses doped with Er3 + and co-doped with Er3 +/Yb3 + ions have been synthesized. The fabricated host was characterized by high thermal stability parameter (ΔT = 125 °C), high transmittance in mid-infrared region and low maximum phonon energy (724 cm− 1). In order to reduce OH− ions impact on the transmittance value at the band of 3.1 μm, the modified synthesis process has been conducted in low vacuum conditions (50–70 mbar). The wide transmittance window from 0.515 to 5.5 μm has been determined in terms of optical parameters. Luminescent properties of Er3 + ions indicated increase of luminescence intensity at the wavelength of 2.7 μm (4I11/2 → 4I13/2) under 980 nm laser diode excitation resulting from OH− reduction. Simultaneously, the addition of ytterbium to glass system has increased emission intensity in mid-infrared band due to Yb3 + → Er3 + energy transfer. According to mid-infrared luminescence measurements, molar ratio of co-dopants in developed glass matrix for the maximum emission intensity has been determined. Glass characterized by the highest mid-IR emission intensity has been used as the active core of produced optical fiber.
Cechy publikacji
original article
peer-reviewed
Inne
System-identifier
idp:102960
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych