Calorimetric measurements of the Ca-Li liquid alloys
PBN-AR
Instytucja
Instytut Metalurgii i Inżynierii Materiałowej im. Aleksandra Krupkowskiego Polskiej Akademii Nauk
Informacje podstawowe
Główny język publikacji
angielski
Czasopismo
Journal of Mining and Metallurgy Section B-Metallurgy (35pkt w roku publikacji)
ISSN
1450-5339
EISSN
Wydawca
TECHNICAL FACULTY, BOR-SERBIA
DOI
URL
Rok publikacji
2017
Numer zeszytu
3
Strony od-do
203-208
Numer tomu
53
Identyfikator DOI
Liczba arkuszy
0,38
Słowa kluczowe
en
Molar mixing enthalpy; Ca-Li system; calorimetry; DTA; Calphad method; thermochemistry.
Streszczenia
Język
en
Treść
An isothermal high-temperature mixing calorimeter was used for the determination of the enthalpy of mixing ΔmixH for liquid Ca-Li solutions, for 63 alloys of different compositions at the four following temperatures: 588 K, 648 K, 820 K and 1159 K. The studies were performed by way of dropping solid metal samples at ambient temperature into liquid alloys, starting from pure elements. In three series, calcium was dropped into liquid lithium, whereas solid Li samples were added into liquid Ca in the fourth series. Because of the high reactivity of the alloy components, all the steps of the experiment were conducted in a high purity argon atmosphere. It was found that the Ca-Li system is characterized by small negative ΔmixH values and its minimal value is lower than -1.5 kJ/mol. Additionally, the differential thermal analysis was used to determine the phase transformation temperature for 11 Ca-Li alloys. Finally, the Calphad method was used to assess the phase diagram, applying the data of these studies as well as all the experimental results available in the literature.
Cechy publikacji
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:855208
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych