Novel sample treatment procedures for the determination of phosphorus in Cu-based alloys using X-ray fluorescence spectrometry to solve the microstructural effect issue
PBN-AR
Instytucja
Sieć Badawcza Łukasiewicz - Instytut Metali Nieżelaznych
Informacje podstawowe
Główny język publikacji
angielski
Czasopismo
X-RAY SPECTROMETRY (20pkt w roku publikacji)
ISSN
0049-8246
EISSN
1097-4539
Wydawca
WILEY-BLACKWELL
DOI
URL
Rok publikacji
2017
Numer zeszytu
6
Strony od-do
554-562
Numer tomu
46
Identyfikator DOI
Liczba arkuszy
0,5
Słowa kluczowe
angielski
Open access
Tryb otwartego dostępu
Inne
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Inna
Czas opublikowania w otwartym dostępie
Razem z publikacją
Data udostępnienia w sposób otwarty
Streszczenia
Język
angielski
Treść
The accurate analysis of hard CuP and CuPAg-type solders using X-ray fluorescence spectrometry is a difficult task. Surface milling, the most common sample preparation method for calibration materials, results in poor accuracy for the phosphorus analysis, as evidenced by the unacceptable values of the root mean square error. Meanwhile, the analysis of real samples provides incorrect results, and microstructural effects are the main source of error. Thus, this effect was negated by considering the information depth of the phosphorus Kα line and the microstructure size of the alloys. Phosphorus was measured using a thin layer of the sample (a thickness of several micrometers). As a result, the analyzed layer was a poor representative of the sample. Two different approaches for solving the microstructural effect issue were proposed. In the first method, the alloy was remelted under controlled conditions to obtain fine-grain samples, which successfully limited the microstructural effects. The second solution used specially prepared thin layer samples, and the sample dissolution eliminated the microstructural effect. Using the developed sample treatment methods resulted in an improvement in the accuracy of the phosphorus calibration curves. This allowed for the correct determination of phosphorus and other alloying elements in the Cu-based alloys with low uncertainties.
Cechy publikacji
original-article
Inne
System-identifier
PX-5a031453d5de02037cc3cefd
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych