Redox properties of polyelectrolyte multilayer modified electrodes: a significant effect of the interactions between the polyelectrolyte layers in the films
PBN-AR
Instytucja
Wydział Chemii (Uniwersytet Warszawski)
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Electrochimica Acta (40pkt w roku publikacji)
ISSN
0013-4686
EISSN
Wydawca
PERGAMON-ELSEVIER SCIENCE LTD
DOI
URL
Rok publikacji
2017
Numer zeszytu
121-131
Strony od-do
Numer tomu
226
Liczba arkuszy
1.11
Autorzy
Słowa kluczowe
en
polyelectrolytes
PEM thickness
PEM permeability
atomic force microscopy
Streszczenia
Język
en
Treść
The layer-by-layer (LbL) sequential adsorption of oppositely charged polyelectrolytes leads to the formation of multilayered films (Polyelectrolyte Multilayer, PEM). Such systems may find application as ultrathin membranes with controlled properties. In this paper we examine different polyelectrolyte multilayers formed from poly-L-lysine (PLL), polyethyleneimine (PEI), poly(sodium 4-styrenesulfonate) (PSS) and alginate (ALG) polyelectrolytes. Film thicknesses for the PLL/PSS, PLL/ALG and PEI/PSS combinations showed similar values of up to 14 nm on mica and ca. 22 nm on platinum surfaces. The PEI/ALG combination formed thicker films with thicknesses of up to 90 nm on mica and ca. 140 nm on platinum surfaces. For the prepared films, the electroactive behavior towards [Fe(CN)6]3?/4? and [Ru(NH3)6]3+/2 ions was monitored. We found that the oxidation/reduction current of [Fe(CN)6]3?/4? ions showed three different modes of behavior which can be described as non-permeability, permeability and accumulation of ions. For [Ru(NH3)6]3+/2+ such a relation was not observed and all of the films remained permeable. The permeability of the thin PEMs seems to depend more strongly on the film composition than the film thickness. The best candidate for encapsulation purposes is proposed.
Cechy publikacji
discipline:Chemia
discipline:Chemistry
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
PBN-R:790216
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych