COLD CRACKING OF S460N STEEL WELDED IN WATER ENVIRONMENT
PBN-AR
Instytucja
Wydział Mechaniczny (Politechnika Gdańska)
Informacje podstawowe
Główny język publikacji
en
Czasopismo
Polish Maritime Research (20pkt w roku publikacji)
ISSN
1233-2585
EISSN
Wydawca
DOI
URL
Rok publikacji
2018
Numer zeszytu
3 (99)
Strony od-do
131-136
Numer tomu
25
Identyfikator DOI
Liczba arkuszy
Słowa kluczowe
UNDERWATER WELDING, WET WELDING, HIGH-STRENGTH LOW-ALLOY STEEL, COLD CRACKING, CTS TEST
Streszczenia
Język
Treść
This paper shows results of weldability testing of fine-grained high -strength low- alloy S460N steel welded in water environment by covered electrodes. The tests were carried out by using the CTS test specimens with fillet welds. Four specimens were welded under water and one specimen in air. Welded joints were subjected to non-destructive visual and penetration tests. The accepted joints were then subjected to macroscopic and microscopic inspection and Vickers hardness measurements as well. The experiments showed that S460N steel welded in water environment is characterized by a high susceptibility to cold cracking.
Inne
System-identifier
146344
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych