Corrosion of cement pastes made of CEM I and CEM III/A caused by a saturated water solution of ammonium chloride after 4 and 25 days of aggressive immersion
PBN-AR
Instytucja
Sieć Badawcza Łukasiewicz - Instytut Ceramiki i Materiałów Budowlanych
Informacje podstawowe
Główny język publikacji
angielski
Czasopismo
CONSTRUCTION AND BUILDING MATERIALS (40pkt w roku publikacji)
ISSN
0950-0618
EISSN
Wydawca
ELSEVIER SCI LTD
DOI
URL
Rok publikacji
2018
Numer zeszytu
Strony od-do
279-289
Numer tomu
170
Liczba arkuszy
Autorzy
Pozostali autorzy
+ 2
Słowa kluczowe
angielski
Corroded hardened cement paste
Ammonium chloride
Porosity
Decalcification
Phase changes
Portland cement
Slag cement
Open access
Tryb otwartego dostępu
Otwarte czasopismo
Wersja tekstu w otwartym dostępie
Wersja opublikowana
Licencja otwartego dostępu
Creative Commons — Uznanie autorstwa
Czas opublikowania w otwartym dostępie
Przed publikacją
Data udostępnienia w sposób otwarty
2018-03-23
Streszczenia
Język
angielski
Treść
One of the most common causes of the decay of concrete structures is contact with aggressive chemical compounds. Fluids containing chlorides and ammonium ions behave aggressively toward reinforced concrete in many environmental engineering structures. Therefore, the highest level of safety should be preserved in the case of industrial sewage treatment plant facilities, which also aim to protect the environment against pollutants. An accelerated test of the degradation of hydrated cement paste, as the most reactive component of concrete, was conducted. Sulfate resistant cement CEM I, slag cement CEM III/A and corrosive saturated ammonium chloride water solution were used. Investigation after 4 and 25 days of immersion found that portlandite dissolution triggered an increase in porosity. Thaumasite crystallized following ettringite dissolution. Another intermediate phase was Friedel’s salt. The final products of cement paste corrosion were found to be gypsum, calcite and vaterite. Porosity was higher in the case of CEM III/A. Chloride ion concentrations and porosity were not the highest in the surface areas, which were in the direct contact with an aggressive solution. Nitrogen crystalline phases were not found.
Cechy publikacji
oryginalny artykuł naukowy
zrecenzowano naukowo
Inne
System-identifier
PX-5c45b005d5de31e408d492e7
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych