An analysis of a reheater failure and a proposal to upgrade the device design
PBN-AR
Instytucja
Sieć Badawcza Łukasiewicz - Instytut Metalurgii Żelaza im. Stanisława Staszica
Informacje podstawowe
Główny język publikacji
angielski
Czasopismo
ENERGIES
ISSN
EISSN
Wydawca
DOI
URL
Rok publikacji
2019
Numer zeszytu
12
Strony od-do
Numer tomu
12
Identyfikator DOI
Liczba arkuszy
Autorzy
Pozostali autorzy
+ 3
Słowa kluczowe
angielski
reheater
rupture
microstructural degradation
failure analysis
Streszczenia
Język
angielski
Treść
The aim of this paper is to present an example of damage to the reheater tubes and conduct the material and numerical analyses to establish the cause of the device failure. Cracks were observed on the first, second, and third tube row. Close to the damaged area, a ferritic structure could be observed with highly degraded bainite areas, characterized by coagulation and coalescence of precipitates. The cause of the damage was analysed using the finite element method (FEM). The big yield of the tube cross-section confirmed that the tube may get damaged during subsequent cycles of the boiler operation, which was also proved by the microstructure testing results. For the reheater under analysis, the tubes have to be lengthened to achieve a reduction in stresses, arising due to thermal loads to values lower than allowable stresses according to Standard EN 13480-3. The modelling results confirmed the correct operation for the upgraded system.
Cechy publikacji
Original article
Original article presents the results of original research or experiment.
Oryginalny artykuł naukowy
Oryginalny artykuł naukowy przedstawia rezultaty oryginalnych badań naukowych lub eksperymentu.
Inne
System-identifier
WOS:000473821400028
CrossrefMetadata from Crossref logo
Cytowania
Liczba prac cytujących tę pracę
Brak danych
Referencje
Liczba prac cytowanych przez tę pracę
Brak danych